Laboratory analysis report on a fractured steering rocking shaft and a car frame part.

Identifier  ExFiles\Box 38\1\  Scan061
Date  14th April 1919
  
X.3465
COPY.
Laboratory.
Mr. Hives.
R.M. 254 ... No. 14.4.19 (C) 2334

RE ONE ROCKING SHAFT(FRACTURED), AND ONE PART OF THE CAR FRAME. X.3440

ANALYSIS.

Steering Rocking Shaft. Car Frame.
Carbon - .31 .28
Manganese - .44 .47
Nickel - 3.42 3.17
Chromium - Nil .10
Phosphorus - .037 .022
Silicon - .14
Sulphur - .042

-----------------

The steering rocking shaft is a rather soft Nickel steel of a composition we do not use at present; it is possible that it is some of the material supplied by the Monkbridge Iron & Steel Co. The hardness number worked out from the formula 7C+2(Mn+Cr{Mr Cra???ster / Mr Chichester})+Ni = 6.47. According to our specification we do not permit a hardness number less than 7.2 for the section employed for this part. The Brinell figure as received was 255.

The car frame material appeared to be about normal in composition, but the surface has been decarburised owing to prolonged annealing. This is, I think, the primary cause of fracture since the Brinell figure for the outside is only in the neighbourhood of 120, whereas the interior is 158. The softness of the material and the decarburisation is confirmed by a microscopic examination and also by heat treatment; under the latter test the exterior gave a Brinell figure (Contd)
  
  