Temperature test report on Reimanol encased tall coils nos. TR1 and TR3.
| Identifier | ExFiles\Box 45\4\ Scan269 | |
| Date | 6th October 1924 | |
| S5. COPY. 6.10.24. TEMPERATURE TEST ON REIMANOL ENCASED TALL COILS NOS. TR{Capt. F. W. Turner - Finance}1 and TR{Capt. F. W. Turner - Finance}3. Both of the above coils have been heated in our electrically heated oven at temperatures of 85º and 100ºC respectively, and the sparking characteristics observed under the same conditions as the previous tests reported in WA.{Mr Wallis}60. The results are as follows :- Coil. Volts. Max.regular sparking gap. TR.{Capt. F. W. Turner - Finance}1 12 6.5 mm. TR{Capt. F. W. Turner - Finance}1. 8 5.5 mm. TR.{Capt. F. W. Turner - Finance}3. 12 6.5 mm. TR{Capt. F. W. Turner - Finance}3. 8 6.0 mm. Temperature of oven 84ºC. TR.{Capt. F. W. Turner - Finance}1 12 6.5 mm. TR.{Capt. F. W. Turner - Finance}1 8 4.5 mm. TR.{Capt. F. W. Turner - Finance}3. 12 6.5 mm. TR.{Capt. F. W. Turner - Finance}3. 8 5.5 mm. Temperature of oven 100 ºC. It will be seen from the above results compared with previous results that the condition and sparking capabilities of these coils at high temperatures has not appreciably altered. EFC/HEW. | ||